Glass fabric with calcium silica HT finish
Glass fabric with calcium silicate HT finish is a high-performance solution for thermal insulation and fire prevention in demanding environments. The combination of durable glass fabric with a specialized calcium silicate coating provides exceptional heat resistance and mechanical stability.
| Material | Glass fabric, made from smooth (GF) or textured (GT) yarns |
| Coating | Calcium Silica HT Finish |
| Coating options | Single-sided or double-sided coated CS HT finish available in various colors |
| Production qualities | 200 - 1200 g/m² |
| Production widths | 1000 - 2000 mm |
| Temperature resistance (fabric) | 600 - 1000+ °C |
| Temperature resistance (coating) | 800 - 1100 °C |
Glass fabric with heat-resistant calcium silicate finish (HT) – Our Trusted Standard Grades
For information on additional grades or our customized coating options, feel free to contact us.
| Quality type | Structure | Temperature resistance (permanent | short-term) | Weave | Standard Width | Data Sheet |
|---|---|---|---|---|---|
| GF430.HT |
E-glass fabric (430 g/m²) double-sided calcium silicate finish (HT), dark grey | 750 °C | 800 °C | Atlas / Satin | 1000 - 2000 mm | |
| GT580.HT/G50 |
E-glass fabric (580 g/m²) double-sided calcium silicate finish (HT), dark grey | 750 °C | 800 °C | Leinwand / Plain | 1000 - 2000 mm | |
| GT640.HT |
E-glass fabric (640 g/m²) double-sided calcium silicate finish (HT), dark grey | 750 °C | 800 °C | Leinwand / Plain | 1000 - 2000 mm | |
| GF660.HT |
E-glass fabric (660 g/m²) double-sided calcium silicate finish (HT), dark grey | 750 °C | 800 °C | Atlas / Satin | 1000 - 2000 mm | |
| GT740.V4A.HT |
E-glass fabric (660 g/m²), reinforced with steel wire double-sided Calcium-Silica HT-Finish | 750 °C | 1000 °C | Leinwand / Plain | 1000 mm | |
| GT1000.V4A.HT |
E-glass fabric (1000 g/m²) double-sided Calcium-Silica HT-Finish | 750 °C | 1000 °C | Leinwand / Plain | 1000 mm | |
| GT1000.HT |
E-glass fabric (1000 g/m²) double-sided calcium silicate finish (HT), dark grey | 850 °C | 1100 °C | Leinwand / Plain | 1000 - 2000 mm | |
| GT1000.HT/BLUE |
E-glass fabric (1000 g/m²) double-sided calcium silicate finish (HT), blue | 850 °C | 1100 °C | Leinwand / Plain | 1000 - 2000 mm | |
| GT1000.HT/RED |
E-glass fabric (1000 g/m²) double-sided calcium silicate finish (HT), red | 850 °C | 1100 °C | Leinwand / Plain | 1000 - 2000 mm | |
| GT1200.HT |
E-glass fabric (1200 g/m²) double-sided calcium silicate finish (HT), dark grey | 750 °C | 1100 °C | Panama | 1000 - 2000 mm | |
| GT1200.V4A.HT |
E-glass fabric (1200 g/m²) double-sided PU-Alufix | 750 °C | 1000 °C | Panama | 1000 mm |
Technical Characteristics
- The calcium silica HT finish increases the temperature resistance of glass fabrics to up to 1100 °C.
- Resistant to high thermal stress from sparks, flames, and welding spatter.
- Glass fabric with calcium silica HT finish is very robust and resistant to mechanical stresses without losing flexibility.
- Glass fabric with calcium silica HT finish is resistant to most chemicals.
- Also available optionally with woven V4A steel reinforcement.
Application Examples
- These fabrics serve as temperature-resistant and non-combustible protective covers for machines and components during grinding and welding operations.
- As a welding protection blanket, welding protection fabric, or welding protection curtain in industrial environments.
- As a heat-resistant mat for soldering or similar processes.
- Base material for custom special fabrications.
Similar products
Insulation fabric made from glass fabric with silicone coating
Insulation fabric made from Glass Fabric with PU Coating
Heat protection and insulation fabric made from glass fabric with aluminum foil
Thermally pretreated (tempered) Glass Fabric
Glass Fabric with Graphite coating
Flame-resistant fabric made from glass fabric with vermiculite coating
Durable glass fabric with V4A wire reinforcement and special coating for extreme operating conditions